Pavement Seals Resources
|
Delastic® Seal Characteristics |
Joint Design Criteria |
Delastic®
Seal |
Nominal Width
(W) |
Nominal Height
(H) |
Max.
Movement1
|
Narrowest
Opening2
|
Widest
Opening3
|
Minimum
Depth (B) |
Typical Installed
Width (A)** |
|
E-437 |
0.437 (11.11) |
0.937 (23.81) |
0.184 (4.67) |
0.187 (4.67) |
0.371 (9.42) |
1.250 (31.75) |
0.250 (6.35) |
|
E-686 |
0.687 (17.46) |
0.687 (17.46) |
0.259 (6.58) |
0.325 (8.26) |
0.584 (14.83) |
1.250 (31.75) |
0.375 (9.525) |
|
E-816 |
0.812 (20.64) |
0.830 (21.08) |
0.348 (8.84) |
0.350 (8.89) |
0.698 (17.73) |
1.500 (38.10) |
0.500 (12.7) |
|
E-1006 |
1 (25.40) |
1 (25.40) |
0.450 (11.43) |
0.400 (10.16) |
0.850 (21.59) |
1.750 (44.45) |
0.500 - 0.5626 (12.7 - 14.2875) |
|
E-1256 |
1.250 (31.75) |
1 (25.40) |
0.612 (15.54) |
0.450 (11.43) |
1.062 (26.97) |
2 (50.80) |
0.625 (15.875) |
|
E-2000 |
2 (50.80) |
1.500 (38.10) |
0.950 (24.13) |
0.750 (19.05) |
1.700 (43.18) |
2.625 (66.68) |
1.125 (28.575) |
|
E-2500 |
2.500 (63.50) |
2.500 (63.50) |
1.350 (34.29) |
0.775 (19.69) |
2.125 (53.98) |
4 (101.60) |
1.375 (34.925) |
|
E-3000 |
3 (76.20) |
2.500 (63.50) |
1.350 (34.29) |
1.200 (30.48) |
2.550 (64.77) |
4.250 (107.95) |
1.750 (44.45) |
|
E-562 |
0.562 (14.29) |
0.625 (15.88) |
0.178 (4.52) |
0.250 (6.35) |
0.478 (12.14) |
1.125 (28.58) |
0.3125 (7.9375) |
|
V-1625 |
1.625 (41.28) |
1.125 (28.58) |
0.781 (19.84) |
0.600 (15.24) |
1.381 (35.08) |
2.375 (60.33) |
0.875 (22.2275) |
|
Bold numbers represent inches; metric (mm) shown in parentheses.
1 Maximum movement which seal will accomodate in joint with correct design.
2 A narrower opening will place excessive stress on the seal and may cause premature failure.
3 A wider opening may not provide sufficient compressive force to hold the seal in place.
** To be used as a reference only. Installed width may vary by project.
|
Physical Properties
|
ASTM D2628 Physical Requirements for Delastic® Pavement Seals |
|
Properties
|
Requirements |
ASTM Test Method
|
|
Tensile Strength, min., psi (MPa) |
2000(13.8) |
D 412 |
|
Elongation at break, min., % |
250 |
D 412 |
|
Hardness, Type A durometer, points |
55+-5 |
D 2240 (modified)A |
Oven aging, 70 h at 212°F (100°C)
Tensile strength, loss, max, %
Elongation, loss, max, %
Hardness, Type A durometer, points change |
20 max
20 max
0 to +10
|
D 573 |
Oil swell, ASTM Oil No. 3, 70 h at 212°F (100°C)
Weight change, max, % |
45 max. |
D 471
|
Ozone Resistance
20% strain, 300 pphm in air, 70 h at 104°F (40°C) |
no cracks |
D 1149(modified)B
|
Low-temperature stiffening, 7 days at 14°F (-10°C)
Hardness, Type A durometer, points change |
0 to +15 |
D 2240
|
Low-temperature recovery, C72 h at 14°F (-10°C)
50% deflection, min, % |
88
|
9.2D
|
Low-temperature recovery, C22 h at -20°F (-29°C)
50% deflection, min, % |
83
|
9.2D
|
High-temperature recovery, C70 h at 212°F (100°C)
50% deflection, min, % |
85
|
9.2D
|
Compression-deflection, at 80% of nominal width,
min, lbf/in. (N/m)
|
3.5 (613) |
9.3D |
More Information
>> Back to Top <<
|